Effect of Organic Matter on Swell and Undrained Shear Strength of Treated Soils

Received: 31 May 2019     Accepted: 1 July 2019     Published: 12 July 2019
Views:       Downloads:
Abstract

This paper presents a laboratory and statistical study on swell and undrained shear strength of cemented organic clays blended with eco-friendly (by-product) cementitious materials such as ground granulated blast slag (GGBS) and cement kiln dust (CKD). The presence of organic matter in soils can be very problematic especially during construction of infrastructures such as roads and foundations. Therefore, experimental and statistical investigations are crucial to further understand the effect of organic matter on swell and strength performance of soils treated with by-product materials (GGBS and CKD). Five artificially synthesised organic clays with 0%, 5%, 10%, 15% and 20% organic matters were mixed with 20% cement during the first phase of mixing. In the second phase, cement content was reduced to 4% and blended with 12% GGBS and 4% CKD respectively. All mixed samples were cured up to 56days and subjected to undrained triaxial test and one-dimensional oedometer swell test. The undrained shear strength of the untreated soils decreases from 22.47kPa to 15.6kPa upon increase in organic matter from 0-20%. While the swell increases from 1.17% to 3.83% for the same range of 0-20% organic matter. The results also show improvement on strength and swell upon addition of 20% cement for all investigated samples. For samples treated with 4% cement and inclusion of 12% GGBS and 4% CKD, the treated soils showed better performance in terms of swell potential due to reduction in plasticity compared to the plasticity of soils treated with 20% cement. Undrained shear strength increases from 632kPa to 804.9kPa and from 549.8kPa to 724.4kPa with reduction in organic matter upon addition of 20% CEM and 4% CEM: 12% GGBS: 4% CKD after 56days. The results obtained show that the inclusion of GGBS and CKD reduced swell and increases undrained shear strength irrespective of the percentage of organic materials due to cementation effect. However, results of the statistical studies show that the presence of organic matter influences the extent of performance of the cement, GGBS and CKD treated soils.

Published in Journal of Civil, Construction and Environmental Engineering (Volume 4, Issue 2)
DOI 10.11648/j.jccee.20190402.12
Page(s) 48-58
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2019. Published by Science Publishing Group

Keywords

Stabilised Soils, Expansive Soils, Organic Matter, Undrained Strength, Swell Capacity, GGBS, Cement, CKD

References
[1] Onitsuka K, Modmoltin C, Kouno M, Negami T. Effect of organic matter on lime and cement stabilized ariake clays. Journal of Geotechnical Engineering 2003: 1–13.
[2] Bennett RH, Lehman L, Hulbert MH, Harvey GR, Bush SA, Forde EB, et al. Interrelationships of organic carbon and submarine sediment geotechnical properties. Marine Geotechnology 1985; 6: 61–98. doi: 10.1080/10641198509388180.
[3] Booth JS, Dahl AG. A note on the relationships between organic matter and some geotechnical properties of a marine sediment. Marine Geotechnology 1986; 6: 281–97. doi: 10.1080/10641198609388191.
[4] Tremblay H, Duchesne J, Locat J, Leroueil S. Influence of the nature of organic compounds on fine soil stabilization with cement. Canadian Geotechnical Journal 2002; 546: 535–46. doi: 10.1139/T02-002.
[5] Morrill LG, Mahilum BC, Mohiuddin SH. Organic compounds in soils : Sorption, degradation and persistence. Ann Arbor Science Publishers; 1982.
[6] Zurairahetty N, Yunus M, Wanatowski D, Hassan NA, Marto A. Shear Strength and Compressibility Behaviour of Lime-treated Organic Clay. KSCE Journal of Civil Engineering 2015; 00: 1–7. doi: 10.1007/s12205-015-0438-5.
[7] Clare KE, Sherwood PT. The effect of organic matter on the setting of soil-cement mixtures. Journal of Applied Chemistry 2007; 4: 625–30. doi: 10.1002/jctb. 5010041107.
[8] Yunus NZM, Wanatowski D, Stace LR. Effect of Humic Acid on Physical and Engineering Properties of Lime-Treated Organic Clay 2011; 5: 724–9.
[9] Banaszkiewicz K, Marcinkowski T. Use of cement-fly ash-based stabilization techniques for the treatment of waste containing aromatic contaminants 2017; 00009. doi: 10.1051/e3sconf/20172200009.
[10] Oliveira P, Correia A, Garcia MR. Effect of Organic Matter Content and Curing Conditions on the Creep Behavior of an Artificially Stabilized Soil. Journal of Materials in Civil Engineering 2016; 25: 864–70. doi: 10.1061/(ASCE) MT. 1943-5533.
[11] Sing WL, Hashim R, Ali FH. Unconfined Compressive Strength of Cemented Peat 2009; 3: 3850–6.
[12] Harris P, Harvey O, Puppala AJ, Sebesta S, Rao S, Saride S. Mitigating the effect of 2009; 7.
[13] Tastan EO, Edil TB, Benson CH, Aydilek AH. Stabilization of Organic Soils with Fly Ash. Journal of Geotechnical and Geoenvironmental Engineering 2011; 137: 819–33. doi: 10.1061/(ASCE) GT. 1943-5606.0000502.
[14] Nath BD, Molla KA, Sarkar G. Study on Strength Behavior of Organic Soil Stabilized with Fly Ash. International Scholarly Research Notices 2017; 2017.
[15] Åhnberg H, Bengtsson P-E, Holm G. Effect of initial loading on the strength of stabilised peat. Proceedings of the Institution of Civil Engineers - Ground Improvement 2001; 5: 35–40. doi: 10.1680/grim. 2001.5.1.35.
[16] Kang G, Tsuchida T, Kim Y, Baek W. Influence of Humic Acid on the Strength Behavior of Cement-Treated Clay during Various Curing Stages 2017; 29: 1–18. doi: 10.1061/(ASCE) MT. 1943-5533.0001919.
[17] Young JF. A review of the mechanisms of set-retardation in portland cement pastes containing organic admixtures. Cement and Concrete Research 1972; 2: 415–33. doi: 10.1016/0008-8846 (72) 90057-9.
[18] Parkkinen E. Utilization of industrial by-products to strengthen soft clayey and organic soils Utilisation des sous-produits de I ’ industrie pour renforcer des sols tendres organiques et argileux. Proceedings of the 14th International Conference on Soil Mechanics and Foundation Engineering (ICSMFE), Hamburg, Germany: 1997, p. 1701–4.
[19] Montgomery DM, Soliars CJ, Perry R, Tariingt SE, Barnes P, Henderson E. Treatment of Organic-Contaminated Industrial Wastes Using Cement-Based Stabilization/Solidification- I. Microstructural Analysis of Cement-Organic Interactions. Waste Management & Research 1991; 9: 103–11.
[20] Kamon M, Tomohisa S, Sawa K. On Stabilization of Hedoro by Using Cement Group Hardening Materials. Jour- Nal of the Society of Materials Science 1989; 432: 1092–7. doi: 10.2472/jsms. 38.1092.
[21] Ahnberg H, Ljungkrantz C, Johansson S-E, Retelitus A, Holmqvist L, Holm G. Cement och kalk för djupstabilisering av jord En kemisk - fysikalisk studie av stabiliseringseffekter. 1995.
[22] Huat BBK, Maail S, Mohamed T. Effect of cement admixtures on the engineering properties of tropical peat soils. American Journal of Applied Sciences 2005; 2: 1113–20. doi: 10.3844/ajassp. 2005.1113.1120.
[23] Chen H, Wang Q. The behaviour of organic matter in the process of soft soil stabilization using cement. Bulletin of Engineering Geology and the Environment 2006; 65: 445–8. doi: 10.1007/s10064-005-0030-1.
[24] Tindall J, Kunkel J. Unsaturated Zone Hydrology for Scientists and Engineers. Prentice Hall, Engelwood Cliffs, New Jersey; 1999.
[25] Phanikumar BR, Sharma RS. Volume change behavior of fly ash-stabilized clays. Journal of Materials in Civil Engineering 2007; 19: 67–75.
[26] Consoli NC, Da Rocha CG, Silvani C. Devising dosages for soil-fly ash-lime blends based on tensile strength controlling equations. Construction and Building Materials 2014; 55: 238–45. doi: 10.1016/j.conbuildmat. 2014.01.044.
[27] Seco A, Ramírez F, Miqueleiz L, García B. Stabilization of expansive soils for use in construction. Applied Clay Science 2011; 51: 348–52.
[28] Khoury NN, Zaman MM. Environmental effects on durability of aggregates stabilized with cementitious materials. Journal of Materials in Civil Engineering 2007; 19: 41–8.
[29] Peethamparan S, Olek J, Lovell J. Influence of chemical and physical characteristics of cement kiln dusts (CKDs) on their hydration behavior and potential suitability for soil stabilization. Cement and Concrete Research 2008; 38: 803–15. doi: 10.1016/j.cemconres. 2008.01.011.
[30] Abbey SJ, Ngambi S, Coakley E. Effect of cement and by-product material inclusion on plasticity of deep mixing improved soils. International Journal of Civil Engineering and Technology 2016; 7: 265–74.
[31] Abbey SJ, Olubanwo AO. Strength and hydraulic conductivity of cement and by-product cementitious materials improved soil. International Journal of Applied Engineering Research 2018; 13: 8684–94.
[32] Abbey SJ, Ng’ambi S, Ganjian E. Development of strength models for prediction of unconfined compressive strength of cement/by-product material improved soils. Geotechnical Testing Journal 2017; 40: 928–35. doi: 10.1520/GTJ20160138.
[33] Eyo EU, Ngambi S, Abbey SJ. Investigative modelling of behaviour of expansive soils improved using soil mixing technique. International Journal of Applied Engineering Research 2017; 12: 3828–36.
[34] Obuzor GN, Kinuthia JM, Robinson RB. Enhancing the durability of flooded low-capacity soils by utilizing lime-activated ground granulated blastfurnace slag (GGBS). Engineering Geology 2011; 123: 179–86. doi: 10.1016/j.enggeo. 2011.07.009.
[35] Celik E, Nalbantoglu Z. Effects of ground granulated blastfurnace slag (GGBS) on the swelling properties of lime-stabilized sulfate-bearing soils. Engineering Geology 2013; 163: 20–5.
[36] Wang D, Zentar R, Abriak NE. Durability and Swelling of Solidified/Stabilized Dredged Marine Soils with Class-F Fly Ash, Cement, and Lime. Journal of Materials in Civil Engineering 2018; 30: 04018013. doi: 10.1061/(ASCE) MT. 1943-5533.0002187.
[37] Erdal Cokca. Use of class C fly ashes for the stabilization of an expansive soil. Journal of Geotechnical and Geoenvironmental Engineering 2001; 127 (7): 568–73. doi: 10.1017/CBO9781107415324.004.
[38] EuroSoilStab. Design Guide Soft Soil Stabilisation. Ct97-0351 1997: 95.
[39] Ganjian E, Jalull G, Sadeghi-Pouya H. Using waste materials and by-products to produce concrete paving blocks. Construction and Building Materials 2015; 77: 270–5. doi: 10.1016/j.conbuildmat. 2014.12.048.
[40] Jalull G, Ganjian E, Sadeghi-Pouya H. Using ground granulated blastfurnace slag and mineral wastes to reduce cement in paving block. Proceedings of Institution of Civil Engineers: Construction Materials 2014; 167. doi: 10.1680/coma. 13.00011.
[41] Puppala AJ, Manosuthikij T, Chittoori B. Swell and shrinkage characterizations of unsaturated expansive clays from Texas. Engineering Geology 2013; 164: 187–94.
[42] Rawlings JO, Pantula SG, Dickey DA. Applied Regression Analysis: A Research Tool, Second Edition. vol. 18. 1998. doi: 10.1007/b98890.
[43] Goodarzi AR, Akbari HR, Salimi M. Enhanced stabilization of highly expansive clays by mixing cement and silica fume. Applied Clay Science 2016; 132–133: 675–84. doi: 10.1016/j. clay. 2016.08.023.
[44] Abbey SJ, Ngambi S, Ngekpe BE. Understanding the performance of deep mixed column improved soils - A review. International Journal of Civil Engineering and Technology 2015; 6: 97–117.
[45] Farouk A, Shahien MM. Ground improvement using soil-cement columns: Experimental investigation. Alexandria Engineering Journal 2013; 52: 733–40. doi: 10.1016/j.aej. 2013.08.009.
[46] Gaafer M, Bassioni H, Mostafa T. Soil Improvement Techniques. International Journal of Scientific & Engineering Research 2015; 6: 217–22.
[47] Wu Z, Deng Y, Liu S, Liu Q, Chen Y, Zha F. Strength and micro-structure evolution of compacted soils modified by admixtures of cement and metakaolin. Applied Clay Science 2016; 127–128: 44–51. doi: 10.1016/j.clay. 2016.03.040.
[48] Shridevi G, Sreerama R. Efficacy of GGBS Stabilized Soil Cushions With and Without Lime in Pavements. International Journal of Emerging Technologies in Computational and Applied Sciences (IJETCAS) 2014: 141–7.
[49] Shao L., Liu S, Du Y, Jing F., Fang L., ‘’Experimental Study on the Stabilization of Organic Clay with Fly Ash and Cement Mixed Method’’, Geocongress 2008: Characterization, Monitoring, and, Modeling Of Geosystems.
[50] Kitazume M, Terashi M. The deep mixing method. 1st editio. CRC Press; 2013.
[51] Al-Swaidani A, Hammoud I, Meziab A. Effect of adding natural pozzolana on geotechnical properties of lime-stabilized clayey soil. Journal of Rock Mechanics and Geotechnical Engineering 2016; 8: 714–25. doi: 10.1016/j.jrmge. 2016. 04. 002.
[52] Jin, F., Wang, F. and Al-Tabbaa, A. (2016). Three-year performance of in-situ solidified/stabilised soil using novel MgO-bearing binders. Chemosphere, 144, pp. 681-688.
[53] Abdel-Salam, A. (2018). Stabilization of peat soil using locally admixture. HBRC Journal, 14 (3), pp. 294-299.
[54] Md Yusof, Z., Mohd Harris, S. and Mohamed, K. (2015). Compressive Strength Improvement of Stabilized Peat Soil by Pond Ash - Hydrated Lime Admixture. Applied Mechanics and Materials, 747, pp. 242-245.
Cite This Article
  • APA Style

    Samuel Jonah Abbey, Adegoke Omotayo Olubanwo, Samson Ngambi, Eyo Umo Eyo, Blessing Oluwaseun Adeleke. (2019). Effect of Organic Matter on Swell and Undrained Shear Strength of Treated Soils. Journal of Civil, Construction and Environmental Engineering, 4(2), 48-58. https://doi.org/10.11648/j.jccee.20190402.12

    Copy | Download

    ACS Style

    Samuel Jonah Abbey; Adegoke Omotayo Olubanwo; Samson Ngambi; Eyo Umo Eyo; Blessing Oluwaseun Adeleke. Effect of Organic Matter on Swell and Undrained Shear Strength of Treated Soils. J. Civ. Constr. Environ. Eng. 2019, 4(2), 48-58. doi: 10.11648/j.jccee.20190402.12

    Copy | Download

    AMA Style

    Samuel Jonah Abbey, Adegoke Omotayo Olubanwo, Samson Ngambi, Eyo Umo Eyo, Blessing Oluwaseun Adeleke. Effect of Organic Matter on Swell and Undrained Shear Strength of Treated Soils. J Civ Constr Environ Eng. 2019;4(2):48-58. doi: 10.11648/j.jccee.20190402.12

    Copy | Download

  • @article{10.11648/j.jccee.20190402.12,
      author = {Samuel Jonah Abbey and Adegoke Omotayo Olubanwo and Samson Ngambi and Eyo Umo Eyo and Blessing Oluwaseun Adeleke},
      title = {Effect of Organic Matter on Swell and Undrained Shear Strength of Treated Soils},
      journal = {Journal of Civil, Construction and Environmental Engineering},
      volume = {4},
      number = {2},
      pages = {48-58},
      doi = {10.11648/j.jccee.20190402.12},
      url = {https://doi.org/10.11648/j.jccee.20190402.12},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.jccee.20190402.12},
      abstract = {This paper presents a laboratory and statistical study on swell and undrained shear strength of cemented organic clays blended with eco-friendly (by-product) cementitious materials such as ground granulated blast slag (GGBS) and cement kiln dust (CKD). The presence of organic matter in soils can be very problematic especially during construction of infrastructures such as roads and foundations. Therefore, experimental and statistical investigations are crucial to further understand the effect of organic matter on swell and strength performance of soils treated with by-product materials (GGBS and CKD). Five artificially synthesised organic clays with 0%, 5%, 10%, 15% and 20% organic matters were mixed with 20% cement during the first phase of mixing. In the second phase, cement content was reduced to 4% and blended with 12% GGBS and 4% CKD respectively. All mixed samples were cured up to 56days and subjected to undrained triaxial test and one-dimensional oedometer swell test. The undrained shear strength of the untreated soils decreases from 22.47kPa to 15.6kPa upon increase in organic matter from 0-20%. While the swell increases from 1.17% to 3.83% for the same range of 0-20% organic matter. The results also show improvement on strength and swell upon addition of 20% cement for all investigated samples. For samples treated with 4% cement and inclusion of 12% GGBS and 4% CKD, the treated soils showed better performance in terms of swell potential due to reduction in plasticity compared to the plasticity of soils treated with 20% cement. Undrained shear strength increases from 632kPa to 804.9kPa and from 549.8kPa to 724.4kPa with reduction in organic matter upon addition of 20% CEM and 4% CEM: 12% GGBS: 4% CKD after 56days. The results obtained show that the inclusion of GGBS and CKD reduced swell and increases undrained shear strength irrespective of the percentage of organic materials due to cementation effect. However, results of the statistical studies show that the presence of organic matter influences the extent of performance of the cement, GGBS and CKD treated soils.},
     year = {2019}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Effect of Organic Matter on Swell and Undrained Shear Strength of Treated Soils
    AU  - Samuel Jonah Abbey
    AU  - Adegoke Omotayo Olubanwo
    AU  - Samson Ngambi
    AU  - Eyo Umo Eyo
    AU  - Blessing Oluwaseun Adeleke
    Y1  - 2019/07/12
    PY  - 2019
    N1  - https://doi.org/10.11648/j.jccee.20190402.12
    DO  - 10.11648/j.jccee.20190402.12
    T2  - Journal of Civil, Construction and Environmental Engineering
    JF  - Journal of Civil, Construction and Environmental Engineering
    JO  - Journal of Civil, Construction and Environmental Engineering
    SP  - 48
    EP  - 58
    PB  - Science Publishing Group
    SN  - 2637-3890
    UR  - https://doi.org/10.11648/j.jccee.20190402.12
    AB  - This paper presents a laboratory and statistical study on swell and undrained shear strength of cemented organic clays blended with eco-friendly (by-product) cementitious materials such as ground granulated blast slag (GGBS) and cement kiln dust (CKD). The presence of organic matter in soils can be very problematic especially during construction of infrastructures such as roads and foundations. Therefore, experimental and statistical investigations are crucial to further understand the effect of organic matter on swell and strength performance of soils treated with by-product materials (GGBS and CKD). Five artificially synthesised organic clays with 0%, 5%, 10%, 15% and 20% organic matters were mixed with 20% cement during the first phase of mixing. In the second phase, cement content was reduced to 4% and blended with 12% GGBS and 4% CKD respectively. All mixed samples were cured up to 56days and subjected to undrained triaxial test and one-dimensional oedometer swell test. The undrained shear strength of the untreated soils decreases from 22.47kPa to 15.6kPa upon increase in organic matter from 0-20%. While the swell increases from 1.17% to 3.83% for the same range of 0-20% organic matter. The results also show improvement on strength and swell upon addition of 20% cement for all investigated samples. For samples treated with 4% cement and inclusion of 12% GGBS and 4% CKD, the treated soils showed better performance in terms of swell potential due to reduction in plasticity compared to the plasticity of soils treated with 20% cement. Undrained shear strength increases from 632kPa to 804.9kPa and from 549.8kPa to 724.4kPa with reduction in organic matter upon addition of 20% CEM and 4% CEM: 12% GGBS: 4% CKD after 56days. The results obtained show that the inclusion of GGBS and CKD reduced swell and increases undrained shear strength irrespective of the percentage of organic materials due to cementation effect. However, results of the statistical studies show that the presence of organic matter influences the extent of performance of the cement, GGBS and CKD treated soils.
    VL  - 4
    IS  - 2
    ER  - 

    Copy | Download

Author Information
  • Civil Engineering Cluster, Department of Geography and Environmental Management, Faculty of Engineering and Technology, University of the West of England, Bristol, United Kingdom

  • School of Energy, Construction and Environment, Faculty of Engineering, Environment and Computing, Coventry University, Coventry, United Kingdom

  • School of Energy, Construction and Environment, Faculty of Engineering, Environment and Computing, Coventry University, Coventry, United Kingdom

  • School of Energy, Construction and Environment, Faculty of Engineering, Environment and Computing, Coventry University, Coventry, United Kingdom

  • Department of Civil Engineering, Faculty of Engineering, Technology and Science, University of South Wales, Cardiff, United Kingdom

  • Sections